Ejectors

Filter
Close filters
1 From 2
No results were found for the filter!
AH,A,Akern.JPG
DIN 1530 form A Copper core pin
Material: special copper alloys (beryllium alloy) Material features: highest thermal conductivity approximately 10 times higher than tool steel, corrosion-resistant, softening temperature: 420 ° C Hardness: Shaft: HB 185-210 The pins can be smoothly rotated to any desired degree and any form, milled or ground. Surface of copper core pins can be coated. Please ask us.
From €24.31 *
AH,A,Akern.JPG
DIN 1530 form A black Ejector pin
nitrided, black, with cylindrical head|material: 1.2343 or 1.2344, start resistance min.600°C. |shaft hardness: surface plasma-nitrided, black oxidized, min. 950 HV. core strength min. 1400 N/mm2.|head hardness: 50 ± 5 HRC
From €3.89 *
NEW
AH,A,Akern.JPG
DIN 1530 form A blank Ejector pin nitrided
nitrided, blank, with cylindrical head|material: 1.2343 or 1.2344, start resistance min.600°C. shaft hardness: surface bad- or gas nitrided, min. 950 HV. core strength min. 1400 N/mm2. |polished surface after nitriding. head hardness: 50 ± 5 HRC
From €3.78 *
AH,A,Akern.JPG
DIN 1530 form A unnitrided Core pin
material 1.2343 oder 1.2344, pre-toughened|head hardness ca. 40 - 45 HRC, blank 50 ± 5 HRC
From €3.77 *
AH.JPG
DIN 1530 form AH Ejector pin
hardened, with cylindrical head material: 1.2210 or 1.2067 or similar, start resistance min.200°C. shaft hardness 60 ±2 HRC, head hardness 45 ± 5 HRC.
From €2.29 *
AH,A,Akern.JPG
DIN 1530 form AH-corrosion resistant Ejector pin
hardened, with cylindrical head| material: 1.4125| shaft hardness 58 + 4 HRC, head hardness 30 +10 HRC| Especially suitable for the medical and food industries|
From €8.35 *
AH,A,Akern.JPG
DIN 1530 form AH-HSS Ejector pin
material: HSS-1.3343 shaft hardness 60 ±1 HRC head hardness 42± 2 HRC These ejector Pins of HSS are heat resistant up to 560 ° C. increase the wear the pins can be nitrided and TIN or TiCN, etc. coated.
From €2.79 *
DIN1530-C.jpg
DIN 1530 form C Ejector pin
nitrided, with cylindrical head|material: 1.2343 or 1.2344, start resistance min.600°C.| shaft hardness: surface bath- or gas-nitrided, min 950 HV.|core strenght min. 1400 N/mm2.| head hardness: 50 ± 5 HRC.
From €8.40 *
DIN1530-C.jpg
DIN 1530 form CH Ejector pin
hardened, with cylindrical head material: 1.2210 or 1.2067 or similar, start resistance min.200°C. shaft hardness 60 ±2 HRC, head hardness 45 ± 5 HRC.
From €7.28 *
DIN1530-D.jpg
DIN 1530 form D Ejector pin
hardened, with conical head material: 1.2210/1.2067 or similar, start resistance min.200°C. shaft hardness 60 ±2 HRC, head hardness 45 ± 5 HRC.
From €1.50 *
M_DIN_1530_FlachausweSt-FA_s62.JPG
DIN 1530 form FA Ejector blade form FA, nitrided
nitrided, with cylindrical head material: 1.2343 or 1.2344, start resistance min.600°C. shaft hardness: surface black//black oxidized, min. 950 HV. |Core strength min. 1400 N/mm². |head hardness: 50 ± 5 HRC
From €20.77 *
M_DIN_1530_FlachausweSt-FAH_s63.JPG
DIN 1530 form FAH Ejector blade form FAH
hardened with cylindrical head|material: 1.2210 oder 1.2067 oder similar, start resistance min. 200°C. |head hardness: 45 ± 5 HRC, shaft hardness: 60 ± 2 HRC
From €16.07 *